Taber Abraser Test Accessories
Article No. 10123
Taber S-34 Zinc Standardization Plate
- Rolled zinc sheet, having a thickness of approximately 0.8 mm.
- Used to verify the abrasion rate of sandpaper strips such as S-42.
- 5 per pack.
Features
- Test Plates - Provide a convenient substrate for coatings and other materials. They should be sprayed, drawn down or control-dipped to achieve a uniform coating. NOTE: When preparing your own test panels, ensure the sides are flat and parallel. A simple means to check for flatness is to place a straight edge across the test panel surface, and verify there is no gap. Use a file to remove any burrs from the center hole and edges.
- Standardization plates are offered and used to determine the abrasion characteristics of specific Taber abradants. Note, the S-34 zinc plate should not be used for more than 10 calibrations per side. 100 mm square with a 6.35 mm center hole.
Technical Attributes
-
- Data
-
S-16 Specimen Plates, Steel - blanked from 20-gage auto body sheet steel and dull finished for good adhesion of the coating to the metal. 100 mm square with rounded corners and a 6.35 mm center hole (10 per pack) S-17 Specimen Plaques, Birch Plywood - grade A1, 6.35 mm birch plywood, sanded on both sides. 100 mm square with a 6.35 mm center hole (10 per pack) S-18 Specimen Plates, Aluminum - #19 gauge 5052 aluminum. 100 mm square with rounded corners and a 6.35 mm center hole (10 per pack) S-34 Standardization Plates, Zinc - rolled zinc sheet, having a thickness of approximately 0.8 mm, used to verify the abrasion rate of sandpaper strips (such as S-33 or S-42). 100 mm square with either a 6.35 mm or 13.5 mm center hole (5 per pack) S-38 Standardization Plates, Plexiglas™ - cell-cast acrylic (PMMA) used to evaluate the abrasion characteristics of grit used with the Taber Grit Feeder Attachment. 100 mm square with a 6.35 mm center hole and protective sheet applied to both sides (10 per pack) NOTE: Refacing Discs should be stored and conditioned in a controlled environment: temperature = 23 °C ±2 °C, relative humidity = 50% ±5%
Reference Plates per ISO 15082 - AS4000S coated polycarbonate used to evaluate the abrasion characteristics of Taber CS-10F wheels 100 mm square with a 6.35 mm center hole and protective sheet applied to both sides (3 per pack)